Gas Tungsten arc welding Low-poly 3D model

Gas tungsten arc welding (GTAW), also known as tungsten inert gas (TIG) welding, is an arc welding process that uses a non-consumable tungsten electrode to produce the weld. The weld area and electrode are protected from oxidation or other atmospheric contamination by an inert shielding gas (argon or helium). A filler metal is normally used, though some welds, known as autogenous welds, or fusion welds do not require it. When helium is used, this is known as heliarc welding. A constant-current welding power supply produces electrical energy, which is conducted across the arc through a column of highly ionized gas and metal vapors known as a plasma. GTAW is most commonly used to weld thin sections of stainless steel and non-ferrous metals such as aluminum, magnesium, and copper alloys. The process grants the operator greater control over the weld than competing processes such as shielded metal arc welding and gas metal arc welding, allowing for stronger, higher quality welds. However, GTAW is comparatively more complex and difficult to master, and furthermore, it is significantly slower than most other welding techniques. A related process, plasma arc welding, uses a slightly different welding torch to create a more focused welding arc and as a result is often automated. After the discovery of the short pulsed electric arc in 1801 by Humphry Davy and of the continuous electric arc in 1802 by Vasily Petrov, arc welding developed slowly. C. L. Coffin had the idea of welding in an inert gas atmosphere in 1890, but even in the early 20th century, welding non-ferrous materials such as aluminum and magnesium remained difficult because these metals react rapidly with the air, resulting in porous, dross-filled welds. Processes using flux-covered electrodes did not satisfactorily protect the weld area from contamination. To solve the problem, bottled inert gases were used in the beginning of the 1930s. A few years later, a direct current, gas-shielded welding process emerged in the aircraft industry for welding magnesium.

Russell Meredith of Northrop Aircraft perfected the process in 1941. Meredith named the process Heliarc because it used a tungsten electrode arc and helium as a shielding gas, but it is often referred to as tungsten inert gas welding (TIG). The American Welding Society's official term is gas tungsten arc welding (GTAW). Linde Air Products developed a wide range of air-cooled and water-cooled torches, gas lenses to improve shielding, and other accessories that increased the use of the process. Initially, the electrode overheated quickly and, despite tungsten's high melting temperature, particles of tungsten were transferred to the weld. To address this problem, the polarity of the electrode was changed from positive to negative, but the change made it unsuitable for welding many non-ferrous materials. Finally, the development of alternating current units made it possible to stabilize the arc and produce high quality aluminum and magnesium welds.

Developments continued during the following decades. Linde developed water-cooled torches that helped prevent overheating when welding with high currents. During the 1950s, as the process continued to gain popularity, some users turned to carbon dioxide as an alternative to the more expensive welding atmospheres consisting of argon and helium, but this proved unacceptable for welding aluminum and magnesium because it reduced weld quality, so it is rarely used with GTAW today. The use of any shielding gas containing an oxygen compound, such as carbon dioxide, quickly contaminates the tungsten electrode, making it unsuitable for the TIG process. In 1953, a new process based on GTAW was developed, called plasma arc welding. It affords greater control and improves weld quality by using a nozzle to focus the electric arc, but is largely limited to automated systems, whereas GTAW remains primarily a manual, hand-held method. Development within the GTAW process has continued as well, and today a number of variations exist. Among the most popular are the pulsed-current, manual programmed, hot-wire, dabber, and increased penetration GTAW methods.